ASME B16.9 ASTM A403 Alloy 400 Stub End DN100 SchXS
Short Description
Model No.: ASME-B16.9-ASTM-A403-Alloy-400-Stub-End-DN100-SchXS
China Lap Joint Stub End Manufacturer www.pipelinedubai.com offers ASME B16.9 ASTM A403 Alloy 400 Stub End, DN100, SchXS.
Key Specifications / Features
Type: Alloy 400 Stub End
Material: Monel 400 (UNS N04400/Alloy 400)
Size: DN100 (4″)
WT: SCHXS
Chemical Composition, % of Monel 400 (UNS N04400/Alloy 400)
| C | Mn | S | Si | Ni | Cu | Fe |
|---|---|---|---|---|---|---|
| .30 max | 2.00 max | .024 max | .50 max | 63.0 min | 28.0-34.0 | 2.50 max |
Properties of Monel 400 (UNS N04400/Alloy 400)
The following table describes the properties of Monel 400.
Relative to other similar metals, it unusually is strong and corrosion-resistant.
| Property | Value (Metric) | Value (Imperial) |
|---|---|---|
| Density | 8.80*103 kg/m3 | 549 lb/ft3 |
| Modulus of Elasticity | 179 GPa | 26,000 ksi |
| Thermal Expansion (20ºC) | 13.9*10-6º C-1 | 7.7*10-6 in/(in*ºF) |
| Specific Heat Capacity | 427 J/(kg*K) | 0.102 BTU/(lb*ºF) |
| Thermal Conductivity | 21.8 W/(m*K) | 151 BTU*in/(hr*ft2*ºF) |
| Electric Resistivity | 54.7*10-8 Ohm*m | 54.7*10-6 Ohm*cm |
| Tensile Strength (Annealed) | 550 MPa | 79,800 psi |
| Yield Strength (Annealed) | 240 MPa | 34,800 psi |
| Elongation | 48% | 48% |
| Liquidus Temperature | 1,350º C | 2,460º F |
| Solidus Temperature | 1,300º C | 2,370º F |
Mechanical Properties
Typical room temperature Tensile Properties of Annealed Material
Dimensions of ASME B16.9 Lap Joint Stub End
Schedule XS
| NPS | OD | T | G | F | R | kg |
| 1/2 | 21.3 | 3.73 | 34.9 | 76.2 | 3.18 | 0.2 |
| 3/4 | 26.7 | 3.91 | 42.9 | 76.2 | 3.18 | 0.3 |
| 1 | 33.4 | 4.55 | 50.8 | 101.6 | 3.18 | 0.4 |
| 1.1/4 | 42.2 | 4.85 | 63.5 | 101.6 | 4.76 | 0.6 |
| 1.1/2 | 48.3 | 5.08 | 73 | 101.6 | 6.35 | 0.7 |
| 2 | 60.3 | 5.54 | 92.1 | 152.4 | 7.94 | 1.4 |
| 2.1/2 | 73 | 7.01 | 104.8 | 152.4 | 7.94 | 2 |
| 3 | 88.9 | 7.62 | 127 | 152.4 | 9.53 | 2.9 |
| 3.1/2 | 101.6 | 8.08 | 139.7 | 152.4 | 9.53 | 3.4 |
| NPS | OD | T | G | F | R | kg |
| 4 | 114.3 | 8.56 | 157.2 | 152.4 | 11.11 | 4.1 |
| 5 | 141.3 | 9.53 | 185.7 | 203.2 | 11.11 | 7.5 |
| 6 | 168.3 | 10.97 | 215.9 | 203.2 | 12.70 | 10 |
| 8 | 219.1 | 12.70 | 269.9 | 203.2 | 12.70 | 16 |
| 10 | 273.1 | 12.70 | 323.9 | 254 | 12.70 | 24 |
| 12 | 323.9 | 12.70 | 381 | 254 | 12.70 | 29 |
| 14 | 355.6 | 12.70 | 412.8 | 304.8 | 12.70 | 38 |
| 16 | 406.4 | 12.70 | 469.9 | 304.8 | 12.70 | 43 |
| 18 | 457.2 | 12.70 | 533.4 | 304.8 | 12.70 | 49 |
| 20 | 508 | 12.70 | 584.2 | 304.8 | 12.70 | 63 |
| 24 | 609.6 | 12.70 | 692.2 | 304.8 | 12.70 | 76 |
Dimensions are in millimeters unless otherwise indicated. Weights are in kilograms and approximately given.
Dimensional Tolerances of Stub Ends ASME B16.9
| Nominal Pipe Size | 1/2 up to 2.1/2 | 3 to 3.1/2 | 4 | 5 to 8 | 10 to 18 | 20 to 24 |
| Outside Diameter at Welding End (OD) |
+ 1.6
– 0.8
|
1.6 | 1.6 |
+ 2.29
– 1.6
|
+ 4.06
– 3.05
|
+ 6.35
– 4.83
|
| Overall Length (F) | 1.6 | 1.6 | 1.6 | 1.6 | 2 | 2 |
| Outside Diameter of Lap (G) |
+ 0
– 0.76
|
+ 0
– 0.76
|
+ 0
– 0.76
|
+ 0
– 0.76
|
+ 0
– 1.6
|
+ 0
– 1.6
|
| Thickness of Lap (T) |
+ 1.52
– 0
|
+ 1.52
– 0
|
+ 1.52
– 0
|
+ 1.52
– 0
|
+ 1.52
– 0
|
+ 1.52
– 0
|
| Fillet Radius of Lap (R) |
+ 0
– 0.76
|
+ 0
– 0.76
|
+ 0
– 1.6
|
+ 0
– 1.6
|
+ 0
– 1.6
|
+ 0
– 1.6
|
| Wall Thickness (t) | Not less than 87.5% of Nominal Wall Thickness | |||||
Dimensional tolerances are in millimeters unless otherwise indicated.
What are the characteristics of Monel 400?
- Resistant to seawater and steam at high temperatures
- Excellent resistance to rapidly flowing brackish water or seawater
- Excellent resistance to stress corrosion cracking in most freshwaters
- Particularly resistant to hydrochloric and hydrofluoric acids when they are de-aerated
- Offers some resistance to hydrochloric and sulfuric acids at modest temperatures and concentrations, but is seldom the material of choice for these acids
- Excellent resistance to neutral and alkaline salt
- Resistance to chloride induced stress corrosion cracking
- Good mechanical properties from sub-zero temperatures up to 1020° F
- High resistance to alkalis
In what applications is Monel 400 used?
- Marine engineering
- Chemical and hydrocarbon processing equipment
- Gasoline and freshwater tanks
- Crude petroleum stills
- De-aerating heaters
- Boiler feed water heaters and other heat exchangers
- Valves, pumps, shafts, fittings, and fasteners
- Industrial heat exchangers
- Chlorinated solvents
- Crude oil distillation towers
Fabrication with Monel 400
UNS N04400 Alloy 400Alloy 400 can easily be welded by gas-tungsten arc, gas metal arc or shielded metal arc processes using appropriate filler metals. There is no need for post weld heat treatment, however, thorough cleaning after welding is critical for optimum corrosion resistance, otherwise there is the risk of contamination and embrittlement.
Finished fabrications can be produced to a wide range of mechanical properties when proper control of the amount of hot or cold working and the selection of appropriate thermal treatments is done.
Like most other nickel alloys, Monel 400 is typically tough to machine and will work harden. However, excellent results can e obtained if you make the correct choices for tooling and machining.