ASME B16.9 ASTM A312 316 NPT Swage Nipple 1 Inch SCH40 3000LBS
Short Description
Model No.: 316-NPT-Swage-Nipple-1-40
China Swage Nipple Manufacturer www.pipelinedubai.com offers ASME B16.9 ASTM A312 316 Swage Nipple, 1 Inch, SCH40.
Key Specifications / Features
Type: Swage Nipple
Material: 316
Standard: ASME B16.9
Wall Thickness: SCH40
Size: 1 Inch
Ends: NPT
| Swage Nipple | |||||||||
| Size | L | S | Size | L | S | ||||
| mm | inch | mm | inch | mm | inch | mm | inch | ||
| 1/8″ | 32 | 1.26 | 13 | 0.52 | 11/4“ | 58 | 2.28 | 46 | 1.81 |
| 1/4″ | 34 | 1.34 | 15 | 0.59 | 11/2“ | 62 | 2.44 | 51 | 2.01 |
| 3/8″ | 36 | 1.42 | 20 | 0.79 | 2″ | 66 | 2.60 | 63 | 2.48 |
| 1/2″ | 42 | 1.65 | 23 | 0.91 | 21/2“ | 73 | 2.87 | 80 | 3.15 |
| 3/4″ | 47 | 1.85 | 29 | 1.14 | 3″ | 86 | 3.39 | 95 | 3.74 |
| 1″ | 52 | 2.05 | 36 | 1.42 | 4″ | 94 | 3.70 | 120 | 4.72 |
Typical chemical composition for 316 stainless steel
|
% |
316 |
316L |
316H |
316Ti |
|
C |
0.0-0.07 |
0.0-0.03 |
0.04-0.08 |
0.0- 0.08 |
|
Mn |
0.0-2.0 |
0-2.0 |
0.0-2.00 |
0.0-2.00 |
|
Si |
0.0-1.0 |
0.0-1.00 |
0.0-1.00 |
0.0- 1.00 |
|
P |
0.0-0.05 |
0.0-0.05 |
0-0.04 |
0.0-0.05 |
|
S |
0.0-0.02 |
0.0-0.02 |
0.0-0.02 |
0.0-0.03 |
|
Cr |
16.50-18.50 |
16.50-18.50 |
16.50-18.50 |
16.50- 18.50 |
|
Mo |
2.00-2.50 |
2.00-2.50 |
2.00-2.50 |
2.00- 2.50 |
|
Ni |
10.00-13.00 |
10.00-13.00 |
10.00-13.00 |
10.50- 14.00 |
|
Ti |
– |
– |
– |
0.40- 0.70 |
|
Fe |
balance |
balance |
balance |
balance |
Typical mechanical properties for 316 stainless steel
|
Grade |
316 Bar and Section (up to 160 mm thick) |
316 Sheet (up to 8 mm thick) | 316 Plate (8 – 75 mm thick) | 316L Bar and Section (up to 160 mm) |
316L Sheet (up to 8 mm thick) |
316 L Plate (8 – 75 mm thick) |
316H Bar (up to 160 mm) |
316Ti Bar(up to 160 mm) |
|
Tensile Strength (MPa) |
500 – 700 |
530 – 680 | 520 – 670 |
500 – 700 |
530 – 680 |
520 – 670 |
490 – 690 |
500 – 700 |
|
Proof Stress (MPa) |
200 Min |
240 Min | 220 Min |
200 Min |
240 Min |
220 Min |
205 Min |
200 Min |
|
Elongation A50 mm |
40 Min % |
40 Min % |
45 Min % |
40 Min % |
40 Min % |
45 Min % |
35 % |
40 Min % |
|
Hardness Brinell |
215 Max HB |
– |
– |
215 Max HB |
– |
– |
– |
215 Max HB |
|
Property |
Value |
|
Density |
8.00 g/cm3 |
|
Melting Point |
1400°C |
|
Modulus of Elasticity |
193 GPa |
|
Electrical Resistivity |
0.074 x 10-6 Ω.m |
|
Thermal Conductivity |
16.3 W/m.K |
|
Thermal Expansion |
15.9 x 10-6 /K |
Corresponds to the following standard designations and specifications:
|
Euronorm |
UNS |
BS |
En |
Grade |
|
1.4401 |
S31600 |
316S31 |
58H |
316 |
|
1.4404 |
S31603 |
316S11 |
– |
316L |
|
– |
S31609 |
316S51 |
– |
316H |
|
1.4571 |
– |
320S31 |
– |
316Ti |